Material | Monel |
Surface Finish | Polished |
Usage | Construction |
Shape | Round |
Size | 6MM TO 350MM DIA |
Single Piece Length | 6 meter |
The chemical composition of MONEL 400 alloy is given in the following table.
Element | Content (%) |
---|---|
Nickel, Ni | Remainder |
Copper, Cu | 28-34 |
Iron, Fe | 2.5 max |
Manganese, Mn | 2 max |
Silicon, Si | 0.5 max |
Carbon, C | 0.3 max |
Sulphur, S | 0.024 |
The following table discusses the physical properties of MONEL 400 alloy.
Properties | Metric | Imperial |
---|---|---|
Density | 8.8 gm/cm3 | 0.318 lb/in3 |
The mechanical properties of MONEL 400 alloy are tabulated below.
Properties | Metric | Imperial |
---|---|---|
Tensile strength(annealed) | 517-620 MPa | 75-90 ksi |
Yield strength | 172-345 MPa | 25-50 ksi |
Modulus of elasticity | 179 GPa | 26000 ksi |
Poisson’s ratio | 0.32 | 0.32 |
*Your information is safe with us.
Minimum Order Quantity | 1 Kilogram |
Material | Monel |
Size/Diameter | >4 inch |
Surface Finish | Polished |
Usage | Construction |
Shape | CUT IN SHAPE |
Usage/Application | Manufacturing |
Diameter | 6MM TO 350MM DIA |
Single Piece Length | 6 meter |
The following table shows the chemical composition of Nickelvac K-500™.
Element | Content (%) |
---|---|
Nickel, Ni | 66 |
Copper, Cu | 29 |
Aluminum, Al | 2.7 |
Iron, Fe | 1 |
Manganese, Mn | 0.7 |
Tungsten, W | 0.6 |
Silicon, Si | 0.25 |
Carbon, C | 0.1 |
Sulfur, S | 0.01 |
The physical properties of Nickelvac K-500™ are outlined in the following table.
Properties | Metric | Imperial |
---|---|---|
Density | 8.45 g/cm³ | 0.305 lb/in³ |
Melting point | 1338°C | 2440°F |
The mechanical properties of Nickelvac K-500™ are given in the following table.
Properties | Metric | Imperial |
---|---|---|
Tensile strength | 1000 MPa | 145000 psi |
Yield strength (at strain 0.200%) | 655 MPa | 95000 psi |
Elongation at break | 22% | 22% |
Reduction of area | 40% | 40% |
Hardness, Rockwell C | 27 | 27 |
Minimum Order Quantity | 1 Kg |
Material Grade | MONEL K500 |
Size/Diameter | 1 inch |
Shape | ROUND |
Size | CUT IN SIZE |
Usage/Application | Manufacturing |
Finishing | BRIGHT/BLACK |
Minimum Order Quantity | 1 Kg |
Material Grade | MONEL K 500 |
Usage/Application | Construction |
Size/Diameter | 1 inch |
Shape | CUT IN SIZE |
Brand | NEPTUNE |
*Your information is safe with us.
Minimum Order Quantity | 1 Kilogram |
Material Grade | MONEL K 500 |
Grade | MONEL |
Size/Diameter | 1 inch |
Brand | NEPTUNE |
Shape | ROUND |
Size | CUT IN SIZE |
Usage/Application | Construction |
Limiting Chemical Composition, %, of MONEL Alloy K-500
Nickel (plus Cobalt) .....................................................63.0 min. Carbon........................................................................0.25 max.
Manganese ...................................................................1.5 max. Iron................................................................................2.0 max.
Sulfur ..........................................................................0.01 max.
Silicon ...........................................................................0.5 max.
Copper ......................................................................27.0 - 33.0
Aluminum ..................................................................2.30 - 3.15
Titanium ....................................................................0.35 - 0.85